Investigation of parent austenite grains from martensite structure using EBSD in a wear resistant steel
Högskolan Dalarna, Akademin Industri och samhälle, Materialteknik. Research and Development, SSAB Europe, Borlänge.
Högskolan Dalarna, Akademin Industri och samhälle, Materialteknik.
2017 (engelsk)Inngår i: Materials, ISSN 1996-1944, E-ISSN 1996-1944, Vol. 10, nr 5, artikkel-id 453Artikkel i tidsskrift (Fagfellevurdert) Published
Abstract [en]

Crystallographic reconstruction of parent austenite grain boundaries from the martensitic microstructure in a wear resistant steel was carried out using electron backscattered diffraction (EBSD). The present study mainly aims to investigate the parent austenite grains from the martensitic structure in an as-rolled (reference) steel sample and samples obtained by quenching at different cooling rates with corresponding dilatometry. Subsequently, this study is to correlate the nearest cooling rate by the dilatometer which yields a similar orientation relationship and substructure as the reference sample. The Kurdjumov-Sachs orientation relationship was used to reconstruct the parent austenite grain boundaries from the martensite boundaries in both reference and dilatometric samples using EBSD crystallographic data. The parent austenite grain boundaries were successfully evaluated from the EBSD data and the corresponding grain sizes were measured. The parent austenite grain boundaries of the reference sample match the sample quenched at 100 °C/s (CR100). Also the martensite substructures and crystallographic textures are similar in these two samples. The results from hardness measurements show that the reference sample exhibits higher hardness than the CR100 sample due to the presence of carbides in the reference sample.

sted, utgiver, år, opplag, sider
MDPI , 2017. Vol. 10, nr 5, artikkel-id 453
Emneord [en]
Dilatometry, Hardness, EBSD, Martensite, Austenite, Kurdjumov-Sachs
HSV kategori
Forskningsprogram
Stålformning och ytteknik
Identifikatorer
URN: urn:nbn:se:du-24715DOI: 10.3390/ma10050453ISI: 000404411000005PubMedID: 28772813OAI: oai:DiVA.org:du-24715DiVA, id: diva2:1088976
Merknad

Open Access APC beslut 10/2017

Tilgjengelig fra: 2017-03-09 Laget: 2017-04-18 Sist oppdatert: 2017-11-29bibliografisk kontrollert
Inngår i avhandling
1. Modelling and Characterisation of the Martensite Formation in Low Alloyed Carbon Steels
Åpne denne publikasjonen i ny fane eller vindu >>Modelling and Characterisation of the Martensite Formation in Low Alloyed Carbon Steels
2017 (engelsk)Licentiatavhandling, med artikler (Annet vitenskapelig)
Abstract [en]

The current work contains experimental and theoretical work about the formation of martensite from the austenitic state of the steel Hardox 450. Simulation of rolling and subsequent quenching of martensitic steel plates requires a model that can account for previous deformation, current stresses and the temperature history, therefore dilatometry experiments were performed, with and without deformation. Two austenitization schedules were used and in the standard dilatometry the cooling rates varied between 5-100 °C/s, in order to find the minimum cooling rate that gives a fully martensitic microstructure. Cooling rates larger than 40°C/s gave a fully martensitic microstructure. The cooling rate of 100 °C/s was used in the deformation dilatometry tests where the uniaxial deformation varied from 5-50 %. The theoretical work involved modelling of the martensite formation and the thermal/transformation strains they cause in the steel. Characterizations were done using light optical microscopy, hardness tests and electron backscatter diffraction technique. The parent austenite grains of the martensitic structure were reconstructed using the orientation relationship between the parent austenite and the martensite. Kurdjumov-Sachs orientation relationships have previously been proven to work well for low-carbon steels and was therefore selected.

The standard implementation of the Koistinen-Marburger equation for martensite formation and a more convenient approach were compared. The latter approach does not require the storage of initial austenite fraction at start of martensite formation. The comparison shows that the latter model works equally well for the martensite formation. The results showed that the use of martensite start and finish temperatures calibrated versus experiments for Hardox 450 works better when computing thermal expansion than use of general relations based on the chemistry of the steel.

The results from deformation dilatometry showed that deformation by compressive uniaxial stresses impedes the martensite transformation. The simplified incremental model works well for deformation with 5 % and 10 %. However, the waviness in the experimental curve for deformation 50 % does not fit the model due vi to large barrelling effect and the large relative expansion for the material that the sample holders are made of.

Crystallographic reconstruction of parent austenite grains were performed on a hot-rolled as-received reference sample and dilatometry samples cooled with 60 °C/s and 100 °C/s. The misorientation results showed that the samples match with the Kurdjumov-Sachs orientation relationship in both hot rolled product and dilatometry samples. When misorientation between adjacent pixels are between 15° and 48°, then the boundary between them was considered as a parent austenite grain. The austenitic grain boundaries of the sample cooled at 100 °C/s is in general identical with the hot rolled sample when considering high angle boundaries (15°-48°). The results from the hardness tests showed that the rolled product exhibits higher hardness as compared to samples cooled by 100 °C/s and 60 °C/s. This can be attributed to the formation of transition-iron-carbides in the hot rolled product due to longer exposure of coiling temperature.

sted, utgiver, år, opplag, sider
Luleå: Luleå University of Technology, 2017. s. 110
Emneord
Dilatometry, Hardness, EBSD, Martensite, Austenite, Kurdjumov-Sachs, Phase transformation, Modelling
HSV kategori
Forskningsprogram
Stålformning och ytteknik
Identifikatorer
urn:nbn:se:du-24714 (URN)978-91-7583-839-7 (ISBN)978-91-7583-840-3 (ISBN)
Presentation
2017-04-28, TDB, Luleå, 10:00 (svensk)
Opponent
Veileder
Tilgjengelig fra: 2017-04-18 Laget: 2017-04-18 Sist oppdatert: 2019-03-06bibliografisk kontrollert

Open Access i DiVA

fulltext(22104 kB)199 nedlastinger
Filinformasjon
Fil FULLTEXT01.pdfFilstørrelse 22104 kBChecksum SHA-512
9e18d6dd0928520947413adcffd87298d3077395e8dce2a9aa97a63cd1da78ae1c351ab385e95456ed14bd08539f05180569116747743f504426b227c6c73047
Type fulltextMimetype application/pdf

Andre lenker

Forlagets fulltekstPubMed

Personposter BETA

Gyhlesten Back, JessicaEngberg, Göran

Søk i DiVA

Av forfatter/redaktør
Gyhlesten Back, JessicaEngberg, Göran
Av organisasjonen
I samme tidsskrift
Materials

Søk utenfor DiVA

GoogleGoogle Scholar
Totalt: 199 nedlastinger
Antall nedlastinger er summen av alle nedlastinger av alle fulltekster. Det kan for eksempel være tidligere versjoner som er ikke lenger tilgjengelige

doi
pubmed
urn-nbn

Altmetric

doi
pubmed
urn-nbn
Totalt: 346 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • chicago-author-date
  • chicago-note-bibliography
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf