Chromium evaporation from plastically deformed pre-coated Sandvik Sanergy HT 22% Cr ferritic interconnect steelShow others and affiliations
2010 (English)In: 2010 Conference Memory Stick 9th European SOFC Forum, Lucerne, 2010Conference paper, Published paper (Other academic) Published
Abstract [en]
Ferritic stainless steel has attracted a great deal of attention for its use as an interconnector in solid oxide fuel cells (SOFCs). The ferritic Sandvik Sanergy HT chromium steel is specially developed for interconnectors in SOFC with a unique chemical composition, which gives the alloy a good high temperature corrosion resistance as well as good surface conductivity in the formed chromium oxide scale. However, chromium evaporation from metallic interconnectors in SOFC fuel cells tends to poison the cathode of the fuel cell. Furthermore, the evaporation of chromium species from the oxide surface tends to increase the oxidation rate resulting in increased contact resistance. It is nowadays well known that thin coatings of e.g. cobalt can substantially reduce the chromium evaporation from the interconnectors.
In this study, a 22% Cr ferritic steel, Sandvik Sanergy HT has been coated with a thin metallic cobalt film. The coated material was plastically deformed and the effect of chromium evaporation was studied as a function of the degree of deformation. Coated samples are also compared to uncoated material. The results show that the metallic cobalt film cracks when the steel sheet is formed but the chromium evaporation is more or less unaffected.
Place, publisher, year, edition, pages
Lucerne, 2010.
Keywords [en]
SOFC, Interconnect, Ferritic stainless steel oxidation, Chromium evaporation, Coatings
Identifiers
URN: urn:nbn:se:du-4707OAI: oai:dalea.du.se:4707DiVA, id: diva2:522129
Conference
9th European SOFC Forum , Lucerne, 29 June- 2 July, 2010
2010-05-232010-05-232012-04-24Bibliographically approved