Dalarna University's logo and link to the university's website

du.sePublications
Change search
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • chicago-author-date
  • chicago-note-bibliography
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf
Studies of effect of glass/silicon powder coatings on clogging behaviour of submerged entry nozzles when using REM alloyed stainless steels
Dalarna University, School of Technology and Business Studies, Material Science.
Dalarna University, School of Technology and Business Studies, Material Science.
2011 (English)In: Ironmaking & steelmaking, ISSN 0301-9233, E-ISSN 1743-2812, Vol. 38, no 3, p. 229-239Article in journal (Refereed) Published
Abstract [en]

The internal surfaces of modern submerged entry nozzles (SENs) were coated with a glass/silicon powder layer to prevent SEN graphite oxidation during preheating. The effects of the interaction between the coating layer and the SEN base refractory materials on clogging were studied. The results indicated that penetration of the formed alkaline rich glaze into the alumina/graphite base refractory occurs during preheating. More specifically, the glaze reacts with graphite to form carbon monoxide gas. Thereafter, dissociation of CO at the SEN/molten metal interface takes place. This leads to reoxidation of dissolved rare earth metals, which form ‘in situ’ rare earth metal oxides at the interface between the SEN and the molten steel. In addition, the interaction of the penetrated glaze with alumina in the SEN base refractory materials leads to the formation of a high viscous alumina rich glaze during the SEN preheating process. This, in turn, creates a very uneven surface at the SEN internal surface. The ‘in situ’ formation of the rare earth metal oxides together with the uneven internal surface of the SEN may facilitate the accumulation of the primary inclusions on the refractory walls.

Place, publisher, year, edition, pages
London,UK: Maney Publishing , 2011. Vol. 38, no 3, p. 229-239
Keywords [en]
Refractory, SEN, Clogging, REM, Coating, Glaze
National Category
Materials Engineering
Research subject
Steel Forming and Surface Engineering, Studier angående bildningsmekanismer för igensättningar i gjutrör
Identifiers
URN: urn:nbn:se:du-5133DOI: 10.1179/1743281210Y.0000000005ISI: 000288320900011Scopus ID: 2-s2.0-79952596989OAI: oai:dalea.du.se:5133DiVA, id: diva2:520285
Available from: 2010-12-09 Created: 2010-12-09 Last updated: 2021-11-12Bibliographically approved
In thesis
1. An Experimental Study of Submerged Entry Nozzles (SEN) Focusing on Decarburization and Clogging
Open this publication in new window or tab >>An Experimental Study of Submerged Entry Nozzles (SEN) Focusing on Decarburization and Clogging
2011 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

The submerged entry nozzle (SEN) is used to transport the molten steel from a tundish to a mould. The main purpose of its usage is to prevent oxygen and nitrogen pick-up by molten steel from the gas. Furthermore, to achieve the desired flow conditions in the mould. Therefore, the SEN can be considered as a vital factor for a stable casting process and the steel quality. In addition, the steelmaking processes occur at high temperatures around 1873 K, so the interaction between the refractory materials of the SEN and molten steel is unavoidable. Therefore, the knowledge of the SEN behaviors during preheating and casting processes is necessary for the design of the steelmaking processes  The internal surfaces of modern SENs are coated with a glass/silicon powder layer to prevent the SEN graphite oxidation during preheating. The effects of the interaction between the coating layer and the SEN base refractory materials on clogging were studied. A large number of accretion samples formed inside alumina-graphite clogged SENs were examined using FEG-SEM-EDS and Feature analysis. The internal coated SENs were used for continuous casting of stainless steel grades alloyed with Rare Earth Metals (REM). The post-mortem study results clearly revealed the formation of a multi-layer accretion. A harmful effect of the SENs decarburization on the accretion thickness was also indicated. In addition, the results indicated a penetration of the formed alkaline-rich glaze into the alumina-graphite base refractory. More specifically, the alkaline-rich glaze reacts with graphite to form a carbon monoxide gas. Thereafter, dissociation of CO at the interface between SEN and molten metal takes place. This leads to reoxidation of dissolved alloying elements such as REM (Rare Earth Metal). This reoxidation forms the “In Situ” REM oxides at the interface between the SEN and the REM alloyed molten steel. Also, the interaction of the penetrated glaze with alumina in the SEN base refractory materials leads to the formation of a high-viscous alumina-rich glaze during the SEN preheating process. This, in turn, creates a very uneven surface at the SEN internal surface. Furthermore, these uneven areas react with dissolved REM in molten steel to form REM aluminates, REM silicates and REM alumina-silicates.

The formation of the large “in-situ” REM oxides and the reaction of the REM alloying elements with the previously mentioned SEN´s uneven areas may provide a large REM-rich surface in contact with the primary inclusions in molten steel. This may facilitate the attraction and agglomeration of the primary REM oxide inclusions on the SEN internal surface and thereafter the clogging. The study revealed the disadvantages of the glass/silicon powder coating applications and the SEN decarburization.

The decarburization behaviors of Al2O3-C, ZrO2-C and MgO-C refractory materials from a commercial Submerged Entry Nozzle (SEN), were also investigated for different gas atmospheres consisting of CO2, O2 and Ar. The gas ratio values were kept the same as it is in a propane combustion flue gas at different Air-Fuel-Ratio (AFR) values for both Air-Fuel and Oxygen-Fuel combustion systems. Laboratory experiments were carried out under nonisothermal conditions followed by isothermal heating. The decarburization ratio (α) values of all three refractory types were determined by measuring the real time weight losses of the samples. The results showed the higher decarburization ratio (α) values increasing for MgO-C refractory when changing the Air-Fuel combustion to Oxygen-Fuel combustion at the same AFR value. It substantiates the SEN preheating advantage at higher temperatures for shorter holding times compared to heating at lower temperatures during longer holding times for Al2O3-C samples. Diffusion models were proposed for estimation of the decarburization rate of an Al2O3-C refractory in the SEN.

Two different methods were studied to prevent the SEN decarburization during preheating: The effect of an ZrSi2 antioxidant and the coexistence of an antioxidant additive and a (4B2O3 ·BaO) glass powder on carbon oxidation for non-isothermal and isothermal heating conditions in a controlled atmosphere. The coexistence of 8 wt% ZrSi2 and 15 wt% (4B2O3 ·BaO) glass powder of the total alumina-graphite refractory base materials, presented the most effective resistance to carbon oxidation. The 121% volume expansion due to the Zircon formation during heating and filling up the open pores by a (4B2O3 ·BaO) glaze during the green body sintering led to an excellent carbon oxidation resistance.

The effects of the plasma spray-PVD coating of the Yttria Stabilized Zirconia (YSZ) powder on the carbon oxidation of the Al2O3-C coated samples were investigated. Trials were performed at non-isothermal heating conditions in a controlled atmosphere. Also, the applied temperature profile for the laboratory trials were defined based on the industrial preheating trials. The controlled atmospheres consisted of CO2, O2 and Ar. The thicknesses of the decarburized layers were measured and examined using light optic microscopy, FEG-SEM and EDS. A 250-290 μm YSZ coating is suggested to be an appropriate coating, as it provides both an even surface as well as prevention of the decarburization even during heating in air. In addition, the interactions between the YSZ coated alumina-graphite refractory base materials in contact with a cerium alloyed molten stainless steel were surveyed. The YSZ coating provided a total prevention of the alumina reduction by cerium. Therefore, the prevention of the first clogging product formed on the surface of the SEN refractory base materials. Therefore, the YSZ plasma-PVD coating can be recommended for coating of the hot surface of the commercial SENs.

Place, publisher, year, edition, pages
Stockholm: KTH Royal Institute of Technology, 2011. p. 87
Keywords
Refractory, SEN, Clogging, REM, Coating, glaze, alkaline, Post- Mortem, industrial preheating, ZrSi2, Graphite, Alumina, Oxidation, Al2O3-C, ZrO2-C, MgO-C, decarburization, reaction mechanism, Yttria Stabilized Zirconia, plasma spray-PVD coating
National Category
Metallurgy and Metallic Materials
Identifiers
urn:nbn:se:du-11703 (URN)978-91-7501-0967-7 (ISBN)
Opponent
Supervisors
Available from: 2013-01-16 Created: 2013-01-16 Last updated: 2015-12-08Bibliographically approved

Open Access in DiVA

No full text in DiVA

Other links

Publisher's full textScopus

Search in DiVA

By author/editor
Memarpour, ArashkBrabie, Voicu
By organisation
Material Science
In the same journal
Ironmaking & steelmaking
Materials Engineering

Search outside of DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetric score

doi
urn-nbn
Total: 905 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • chicago-author-date
  • chicago-note-bibliography
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf